| Coil Width[卷材宽度] | 0.5mm |
| Purity[纯度] | 99.95% |
| Temper[状态] | As Rolled |
| Thickness[厚度] | 0.035mm |
| Typical Analysis(典型分析) |
| C | 30 PPM |
| Ca | <20 PPM |
| Cu | <20 PPM |
| Fe | 20 PPM |
| H | 6 PPM |
| Mg | <10 PPM |
| Mo | 150 PPM |
| N | 10 PPM |
| Ni | <20 PPM |
| O | 30 PPM |
| Pb | <50 PPM |
| Si | <50 PPM |
| Sn | <30 PPM |
| Ti | <20 PPM |
| Mechanical Properties(机械性能) |
| Bulk modulus ( GPa ) ( Hard ) | 311.0 |
| Bulk modulus ( GPa ) ( Soft ) | 311.0 |
| Hardness - Vickers ( kgf mm⁻2 ) ( Hard ) | 500 |
| Hardness - Vickers ( kgf mm⁻2 ) ( Soft ) | 360 |
| Material condition | Soft |
| Material condition | Hard |
| Poisson's ratio ( Hard ) | 0.280 |
| Poisson's ratio ( Soft ) | 0.280 |
| Tensile modulus ( GPa ) ( Hard ) | 411.00 |
| Tensile modulus ( GPa ) ( Soft ) | 411.00 |
| Tensile strength ( MPa ) ( Hard ) | 1920.00 |
| Tensile strength ( MPa ) ( Soft ) | 550.00 - 620.00 |
| Yield strength ( MPa ) ( Soft ) | 550.0 |
| Atomic Properties(原子属性) |
| Atomic number | 74 |
| Atomic weight ( amu ) | 183.85000 |
| Crystal structure | Body Centred Cubic |
| Electronic structure | Xe4f1⁴5d⁴6s2 |
| Ionisation potential ( No./eV ) | 1 / 7.98 |
| Ionisation potential ( No./eV ) | 2 / 17.7 |
| Natural isotope distribution ( Mass No./% ) | 183 / 14.3 |
| Natural isotope distribution ( Mass No./% ) | 182 / 26.3 |
| Natural isotope distribution ( Mass No./% ) | 186 / 28.6 |
| Natural isotope distribution ( Mass No./% ) | 180 / 0.1 |
| Natural isotope distribution ( Mass No./% ) | 184 / 30.7 |
| Photo-electric work function ( eV ) | 4.55 |
| Thermal neutron absorption cross-section ( Barns ) | 18.5000 |
| Valences shown | 2 ,3,4,5,6 |
| Electrical Properties(电气特性) |
| Electrical resistivity ( μOhmcm ) | 5.4@20℃ |
| Superconductivity critical temperature ( K ) | 0.0154 |
| Temperature coefficient ( K⁻1 ) | 0.00480 @0-100℃ |
| Thermal emf against Pt (cold 0C - hot 100C) ( mV ) | 1.12 |
| Thermal Properties(热性能) |
| Coefficient of thermal expansion ( x10⁻⁶ K⁻1 ) | 4.500 @0-100℃ |
| Latent heat of evaporation ( J g⁻1 ) | 4009 |
| Latent heat of fusion ( J g⁻1 ) | 192.00 |
| Melting point ( C ) | 3410.00 |
| Specific heat ( J K⁻1 kg⁻1 ) | 133.0 @25℃ |
| Thermal conductivity ( W m⁻1 K⁻1 ) | 173.00 @0-100℃ |
| Physical Properties(物理性质) |
| Boiling point ( C ) | 5660 |
| Density ( g cm⁻3 ) | 19.300 @20℃ |